Additional file 1: Table S1. of Enhanced Photoelectrochemical Behavior of H-TiO2 Nanorods Hydrogenated by Controlled and Local Rapid Thermal Annealing
journal contribution
posted on 2017-05-05, 05:00 authored by Xiaodan Wang, Sonia EstradÊ, Yuanjing Lin, Feng Yu, Lluis Lopez-Conesa, Hao Zhou, Sanjeev Gurram, Francesca Peiró, Zhiyong Fan, Hao Shen, Lothar Schaefer, Guenter Braeuer, Andreas WaagDonor density (Nd), flat band potential (Vfb) and depletion region width (W) of pristine TiO2 and H-TiO2 nanorods calculated from the Mott-Schottky plots. Figure S1. (a) Optical absorption spectra of pristine TiO2 and H-TiO2 nanorods. (b) Tauc plots of optical absorption curves for pristine TiO2 and H-TiO2 nanorods. Figure S2. Photoconversion efficiency of pristine TiO2 and H-TiO2 nanorods. Figure S3. The O/Ti ratio distribution along the nanorod diameter (a) pristine TiO2 and (b) H-TiO2 nanorods treated at 400 °C. The O/Ti ratio is estimated using EELS spectra taken from a cross-line shown in the TEM image. (DOCX 930 kb)